PLA-LW is primarily used for lightweight components and is widely applied in DIY model aircraft, drones, and cosplay props due to its low density and foaming properties.3DEA PLA-LW Diameter 1.75mm2 ±0.03 Print Temp 190-260ºC (please read description) Hot bed 45-60ºC (optional)Surface: Masking paper, PVP solid glue, glass board, carbon fibre board, PEIProduct features: Low density, up to 0.54g/cm3 The foaming volume ratio is 220%, and 1 roll of 3DEA PLA-LW is equivalent to 2.2 rolls of ordinary PLA Free adjustment of strength and foaming ratio The excellent surface effect, matte and delicate Good adhesion between layers, resistance to explosion and easy to repair Easy to paint, strong surface paint adhesion Excellent printability, large models do not warp, do not block, and do not need a constant temperature chamberProduct parameters:Physical performance indicators of unfoamed consumables: 3D PRINTING FILAMENTTest MethodPLA-LWMelt Flow Index(g/10min)GB/T 3682-20008.1(190℃/2.16kg)DensityGB/T 1033-861.2g/cm3IZOD Impact Strength(kJ/㎡）GB/T 1843-968.58kJ/㎡Tensile Strength(MPa）GB/T 1040-9232.2MPaElongation at Break(%)GB/T 1040-9268.9%Flexural Strength(MPa)GB/T 9341-200041.31MPaFlexural Modulus(MPa)GB/T 9341-20001701MPaPrinting parametersFilamentPLA-LWRecommended printing temperature190-270℃Unfoamed printing temperature190℃Foam printing temperature200-260℃Maximum foaming temperature260℃Maximum foaming rate (260℃)122%Lowest extrusion rate (270℃)45% Bed temperature45-60°C/No heating (Masking paper, PVP solid glue, glass board, carbon fibre board, PEI)Printing speed30-60mm/s Note: Printing test conditions: nozzle 190-280℃; layer height 0.2mm; bed 45℃; speed 40mm/s With different temperature foaming ratio:Temperature/℃200210220230240250260270280Foaming rate/